Specification |
Treatment type |
Main application |
YRK5 |
NO, raw mineral powder |
PE PP EPDM rubber and so on |
YRK4A |
compound vinyl silane. |
plastic. such as PE,PP EPDM and Rubber and so on |
YRK4C |
stearic acid |
PVC,PE Copolymer and Rubber and so on |
YRK4N |
compound amino silane |
PA,TPE and Polarity PE copolymer(EVA EEA etc) and also Rubber and so on |
YRK4 |
NO, raw mineral powder |
PE PP EPDM rubber and son on |
YRK3 |
NO, raw mineral powder |
PE PP EPDM rubber and son on |
YRK2 |
NO, raw mineral powder |
PE PP EPDM rubber and son on |
YRK1 |
NO, raw mineral powder |
PE PP EPDM rubber and son on |
1.YRK4A serial Magnesium hydroxide fire-retardant is high purity Mg(OH)2,,the surface is specially treated with Compound Vinyl Silane
2.because surface is after organic reaction, so it greatly reduces surface energy, and improves the dispersion and liquidity in organic matter accordingly
3.as a no halogen flame retardant, it can be used in plastic. such as PE,PP EPDM ,Rubber. Low smoke density and high thermal stability. initial degradation temperature is about 340 degrees centigrade. No Poisonous and causticity air when degradation.
4.Because of compound vinyl silane surface treatment, it is good for improving the compatibility of polymer and filler when casting mold and modification.
5.With pretreatment of powder when chemical reaction, it will deduce clients’ input for facility and processing steps. further Lower the cost of facility and labor
physical status | white powder |
Mg(OH)2 | Min 91.35% |
CaO | Max 2% |
SiO2 | Max 3.5% |
Fe2O3 | Max 0.5% |
Whiteness | Min 92 |
drying shrinkage(120 degree centigrade,1h) | Max 1% |
D50(particle size) | 2.5-4μm |
loss on ignition(900 degree centigrade) | Min 30% |
mohs hardness | 2.5 |
Initial dehydration temperature |
340 degree centigrade |