Vinyl Silane coated Magnesium Hydroxide Flame Retardant YR6A

  • 产品名称: Vinyl Silane coated Magnesium Hydroxide Flame Retardant YR6A
  • 产品分类: Magnesium Hydroxide By Chemical Method
  • 公司名称: 山东银瑞阻燃材料有限公司
  • 型号规格: YR6A
  • 产品用途: PE,PP,EPDM Rubber and so on
  • 产品价格: ¥0.0
  • 添加时间: 17/08/25
  • 分    享:
产品详情
询盘

Vinyl Silane coated Magnesium Hydroxide Flame Retardant YR6A


Magnesium hydroxide by Chemical method:

Specification

Treatment type

Main application

YR6

NO

PE,PP,EPDM Rubber and so on

YR6A

Vinyl silane

PE,PP,EPDM Rubber and so on

YR6C

stearic acid

PVC,PE Copolymer and Rubber and so on

YR6E

Compound vinyl silane

PE,PP EPDM ,Rubber and so on

YR6N

compound  amino silane

PE,PP,EPDM Rubber and so on

YR6G

Polymer

PE,PP and so on



YR6A Magnesium Hydroxide
Features and Main application:

1.YR6A Serail Magnesium hydroxide fire-retardant is high purity Mg(OH)2,the surface is specially treated with vinyl silane


2.because surface is after organic reaction,so it greatly reduces surface energy, and improves the dispersion and liquidity in organic matter accordingly,
 
3.as a no halogen flame retardant,it can be used in plastic. such as PE,PP EPDM ,Rubber.Low smoke density and high thermal stability. initial decomposition temperature  is about 340 degrees centigrade.No Poisonous and causticity air when degradation.
 
4.Because of vinylsilane surface treatment,it is good for improving the compatibility of polymer and filler when casting mold and modification.
 
5.With pretreatment of powder when chemical reaction,it will deduce clients' input for facility and processing steps.further Lower the cost of facility and labor

Technical parameters:

Physical status

white powder

Mg(OH)2

99.6%

CaO

Max 0.03%

Cl

Max 0.005%

Fe

Max 0.005%

Whiteness

Min 97

drying shrinkage(120 degree centigrade,1h)

0.05%

D50(particle size)

0.7-1.1μm

particle shape

hexagonal platelet

insoluble matter in hydrochloric acid

0.006%

loss on ignition(900 degree centigrade)

Min 30.5%

specific surface area

6-8 m2/g

mohs hardness

2.5

bulk density

300-500 kg/m3

Initial dehydration temperature

340 degree centigrade

electrical conductivity

391 uS/cm